开式整体叶盘四坐标高效开槽插铣工艺方法

 整体叶盘的加工余量主要是在其通道开槽粗加工阶段去除的,提高通道开槽切削效率是实现叶盘高效加工的关键。根据开式整体叶盘通道的结构特点,提出了四坐标插铣开槽高效低成本粗加工方法。通过叶盘叶片偏置面的直纹包络面逼近,确定叶盘通道粗加工区域,给出了四坐标插铣刀位轨迹生成算法。该方法有效解决了直纹面逼近的曲面边界问题,并通过对叶片偏置面的直纹逼近从根本上避免了刀位轨迹计算时误差的产生。实验表明,与传统的侧铣开槽粗加工相比,采用四坐标插铣方式切削力可降低60%,粗加工效率可提高1倍以上。     

基于粘弹性材料的五轴铣削加工被动抑振技术

针对薄壁件在铣削过程中极易出现颤振,且动力学特性快速变化导致切削稳定性多变的特点,研究基于粘弹性材料的被动阻尼技术,以增加薄壁零件阻尼、提升切削稳定性。提出阻尼层、约束层以及质量层的设计方案,模态试验表明该技术能大幅提升薄壁件阻尼,且对多阶振动模态有抑制作用。最后,将其应用于薄壁S样件的五轴铣削加工试验,多组切削参数下的试验结果表明,工件切削振动幅值最大可下降约97%。     

热塑弹性体铝合金化学铣切保护涂料的研制

采用热塑性弹性体为基体材料制备不同配方的铝合金化学铣切保护涂料.实验包括涂料中酚醛树脂的合成,涂料的制备.所做涂料的性能考核包括外观、粘度、固体含量、抗张性、断裂伸长率、浸蚀比、致密性、剥离强度等.最后与美国同类产品性能对比.研究表明,自制的铝合金化学铣切保护涂料的涂膜透明均匀、剥离强度大小适中、耐强碱,满足化学铣切工艺要求,也基本上与美国同类产品性能相当.     

阶梯对称铣削工艺在薄壁件精密加工中的应用

提出了薄壁件精密加工的阶梯对称加工工艺,分析了该工艺的优点及原理,并进行了切削试验,验证了该工艺的有效性。     

基于铣抛喷组合工艺的TB6钛合金精铣参数优化

TB6钛合金是航空制造领域承重结构件的重要材料,属于典型难加工材料。开展了TB6钛合金铣抛喷组合工艺试验,研究了不同铣削参数对表面完整性的影响及精铣与喷丸工序间的耦合关系。结果表明,试件表面粗糙度主要受铣削每齿进给量fz影响。fz0.2mm/z时,组合工艺加工后,试件表面粗糙度值Ra较低;fz0.2mm/z时,随精铣fz提高,铣削硬化率下降,喷丸后的表面粗糙度提高;铣喷组合工艺条件下,铣削线速度vs在20~40m/min范围内,硬化率随vs的升高而降低,喷丸区域表面粗糙度升高;vs在40~50m/min范围内,铣削硬化率升高,喷丸区域表面粗糙度降低。切宽ae对试件硬化和表面粗糙度的影响不显著。铣喷组合工艺条件下的精铣参数优化结果为:vs=50m/min,fz=0.2mm/z,ae=1.0mm。铣抛喷组合工艺条件下,可在低于0.4mm/z范围内适当提高铣削每齿进给量fz。     

CFRP铣削力建模研究

碳纤维增强复合材料(Carbon fiber reinforced polymer/plastic,CFRP)由于其不均匀性和各向异性的材料特性,在铣削加工过程中容易出现各种缺陷。铣削力建模有助于探究CFRP的铣削力变化规律、优化加工参数,进而减少缺陷的产生。本文基于多元非线性回归的方法,建立了铣削力系数关于4种影响因素(纤维切削角、瞬时未变形切屑厚度、主轴转速和轴向切深)的函数关系。经过单向CFRP铣削力实验和多向CFRP铣削力实验验证,所建模型可以较准确地预测铣削力变化规律。     

插铣技术在诱导轮加工中的应用

介绍了采用UG TCL程序算法计算仿真插铣诱导轮的加工工艺.通过DEFORM软件计算插铣诱导轮工艺参数,并经工艺优化得到了一套插铣加工诱导轮的最佳工艺规范.采用该规范加工的诱导轮满足设计要求.装配该诱导轮的发动机通过了热试车考核.     

Tool Life and Surface Integrity in High-speed Milling of Titanium Alloy TA15 with PCD/PCBN Tools

Titanium alloys are widely used in aeronautics that demand a good combination of high strength, good corrosion resistance and low mass. The mechanical properties lead to challenges in machining operations such as high process temperature as well as rapidly increasing tool wear. The conventional tool materials are not able to maintain their hardness and other mechanical properties at higher cutting temperatures encountered in high speed machining. In this work, the new material tools, which are polycrystalline diamond (PCD) and polycrystalline cubic boron nitride (PCBN) tools, are used in high-speed milling of Ti-6.5Al-2Zr-1Mo-1V (TA15) alloy. The performance and wear mechanism of the tools are investigated. Compared to PCBN tool, PCD tool has a much longer tool life, especially at higher cutting speeds. Analyses based on the SEM and EDX suggest that attrition, adhesion and diffusion are the main wear mechanisms of PCD and PCBN tools in high-speed milling of TA15. Oxidation wear is also observed at PCBN tool/workpiece interface. Roughness, defects, micro-hardness and microstructure of the machined surface are investigated. The recorded surface roughness values with PCD/PCBN tools are bellow 0.3 μm at initial and steady cutting stage. Micro-hardness analysis shows that the machined surface hardening depth with PCD and PCBN tools is small. There is no evidence of sub-surface defects with PCD and PCBN tools. It is concluded that for TA15 alloy, high-speed milling can be carried out with PCD/PCBN tools.     

起落架大型承力构件钛合金TC18高效粗加工铣削技术

在简要分析了钛合金TC18材料可加工性差、加工效率低下的基础上,结合飞机起落架大型承力构件的加工特点,对钛合金TC18高效粗加工技术进行了深入研究。通过对粗加工中铣削方式的探究——如何根据机床刚性合理采用强力铣削、大进给铣削的加工方式,大型锻件在编程时的注意事项,以及合理的刀具应用等,实现了TC18大型承力构件的高效铣削粗加工,达到了高的金属去除率。     

基于微小型机床的微细铣削力实验研究

在自行开发的三轴联动微小型铣床上,对铝合金材料2A12进行了微细铣削力实验.采用单因素方法,研究了微细槽铣时主轴转速、轴向切削深度、每齿进给量对切削力的影响,以及微细顺铣和逆铣时径向切削深度对切削力的影响,并对切削力信号进行频谱分析.